Abstract
A systematic study on irradiation induced lattice expansion and subsequent lattice relaxation by post-irradiation annealing was reported. The XRD observations were accompanied by electron-energy loss spectroscopy experiments in TEM. It was concluded that the lattice relaxation upon annealing is likely due annihilation of O vacancies but also due to annihilation of irradiation damage.
Details
Original language | English |
---|
Pages (from-to) | 1555-1562 |
---|
Journal | Journal of Materials Research |
---|
Volume | 30 |
---|
Issue number | 9 |
---|
DOIs | |
---|
Publication status | Published - 14 May 2015 |
---|