Deuterium retention in tungsten and tungsten-tantalum alloys exposed to high-flux deuterium plasmas

Research output: Contribution to journalArticle

Authors

Documents & links

DOI

Abstract

A direct comparison of deuterium retention in samples of tungsten and tungsten–tantalum alloys (W1%Ta,W–5%Ta), exposed to deuterium plasmas (ion flux 1024m−2s−1, ion energy at the biased target ∼50eV) at the plasma generator Pilot-PSI was performed using thermal desorption spectroscopy (TDS). No systematic difference in terms of total retention was identified. The measured retention value for each grade did not deviate by more than 24% from the value averaged over the three grades exposed to the same conditions. No additional desorption peaks appeared in the TDS spectra of the W–Ta samples as compared with the W target, indicating that no additional kinds of traps are introduced by the alloying of W with Ta. The same samples were exposed to the same plasma conditions several times, demonstrating that samples with the history of prior exposures yield an increase in deuterium retention of up to 130% under the investigated conditions compared with the samples that were not exposed before. Exposure of the considered materials to ions with energy below the displacement threshold generates additional traps for deuterium. The positions of the release peaks caused by these traps are similar forWandWTa, which indicates that the traps are of the same kind.

Details

Original languageEnglish
Pages (from-to)103021-103021
JournalNuclear Fusion
Volume52
Issue number10
DOIs
StatePublished - 29 Aug 2012

Keywords

  • fusion, tungsten and alloys, retention

ID: 141969