environmentally assisted cracking of Eurofer97 in water

Research output: Contribution to journalArticle

Institutes & Expert groups

Documents & links

Abstract

Environmentally assisted cracking of Eurofer 97 in fusion reactor conditions is being considered in two environments, namely high temperature water and eutectic liquid Pb–Li alloy. For both stress corrosion cracking (SCC) as well as liquid metal embrittlement (LME), the yield stress of the material has been identified as a key parameter. Neutron irradiation is an important factor in determining the yield stress of materials in reactor components during their service. In this work, the influence of irradiation on the mechanical behaviour and stress corrosion cracking in water is reviewed. It is shown that proper water chemistry control is able to suppress the occurrence of SCC in irradiated materials. This result allows to formulate safe operating conditions for mildly irradiated components with respect to stress corrosion cracking.

Details

Original languageEnglish
Pages (from-to)973-977
Journalfusion engineering and design
Volume75-79
Publication statusPublished - 18 Aug 2005

Keywords

  • eurofer97, environmentally assisted cracking

ID: 199955