Use of Miniaturized Compact Tension Specimens for Fracture Toughness Measurements in the Upper Shelf Regime

Research output: Report/bookBLG - Open report

Documents & links

Documents

Abstract

In the nuclear field, the importance of direct fracture toughness measurements on RPV materials has been nowadays widely recognized, as opposed to Charpy-based estimations. However, sample dimensions have to be kept small in order to optimize the use of available material (often in the form of previously broken Charpy specimens) or, in the case of new irradiations, make effective use of the limited space available inside irradiation facilities. One of the most appealing geometries for fracture toughness measurements is the miniature Compact Tension specimen, MC(T), which has the following dimensions: B = 4.15 mm, W = 8.3 mm, cross section 10 × 10 mm². Four MC(T) specimens can be machined out of a broken half Charpy, and in the case of irradiation ten MC(T) samples occupy approximately the same volume as a full-size Charpy specimen. The MC(T) geometry was already successfully applied and qualified for fracture toughness assessments in the ductile-to-brittle transition regime, using the Master Curve method (ASTM E1921-03). A further, comprehensive investigation is presented in this report, aimed at assessing the applicability of MC(T) specimens to measure fracture toughness in fully ductile (upper shelf) conditions. In this study, 18 1TC(T) and 20 MC(T) specimens have been tested at different temperatures from three RPV steels and one low-alloy C-Mn steel. The results obtained clearly show that MC(T) samples exhibit lower fracture toughness properties, both in terms of initiation of ductile tearing (according to various test standards) and resistance to ductile crack propagation (J-R curve). The reduction of tearing resistance might be attributed to work hardening prevailing over loss of constraint in the uncracked ligament in a side-grooved specimen, or to the inadequacy of J-integral to represent ductile crack extension in very small specimens. Both arguments will have to be verified with further investigations.

Details

Original languageEnglish
PublisherBelgian Nuclear Research Center
Number of pages44
Volume1
Edition0
Publication statusPublished - 12 Apr 2005

Publication series

NameSCK•CEN Reports
PublisherStudiecentrum voor Kernenergie
No.BLG-1009

Keywords

  • Upper shelf fracture toughness measurement, miniature Compact Tension specimen, ductile tearing initiation, J-R curve, work hardening, loss of constraint

ID: 357062